液硫池防腐层失效原因分析及修复措施

目的 液硫池作为硫磺回收装置重要的硫磺储存和脱气处理设施,运行环境恶劣,易发生防腐层失效等问题,影响装置安全运行.因此,提出了解决液硫池防腐层失效问题的预防及修复措施.方法 通过行业调研,总结了液硫池防腐层的主要失效形式、易发生失效的部位等.采用理论分析、样品分析等方式对失效原因进行了分析,提出了液硫池防腐层失效机理和...

Failure cause analysis and repair measures of anticorrosive coating for liquid sulfur pool

ObjectiveThe liquid sulfur pool is important sulfur storage and degassing treatment facility for sulfur recovery unit, which has poor operation environment and is easily result to failure of anticorrosive coating, so it will affect the safe operation of the unit. Therefore, the prevention and repair measures were put forward to solve the failure of liquid sulfur pool anticorrosion coating. MethodsThrough industry investigation, the main failure forms and parts prone to failure of liquid sulfur poor anticorrosive coating were summarized. The failure reasons were analyzed by theoretical analysis and sample analysis, and the failure mechanism and development process of liquid sulfur poor anticorrosive coating were put forward. The restoration plan of adding stainless steel lining was determined by field test. ResultsThe field test results showed that the stainless steel lining worked well and the parameters were improved obviously. ConclusionsThe main reasons for the failure of anticorrosive coating in liquid sulfur poor were water seepage, poor insulation effect, H₂S explosion and poor construction quality. The inner stainless steel plate completely solved the problems of corrosive coating damage and water seepage, which provided a reference for similar devices.