Near-Neutral pH Stress Corrosion Cracking Susceptibility of Plastically Prestrained X70 Steel Weldment |
| |
Authors: | Baotong Lu Jing-Li Luo Douglas G Ivey |
| |
Affiliation: | (1) Department of Chemical and Materials Engineering, University of Alberta, Edmonton, AB, Canada, T6G 2V4;(2) Present address: Southwest Research Institute, San Antonio, TX 78238, USA; |
| |
Abstract: | The application of strain-based design for pipelines requires comprehensive understanding of the postyield mechanical behavior
of materials. In this article, the impact of plastic prestrain on near-neutral pH stress corrosion cracking (SCC) susceptibility
of welded X70 steel was investigated with a slow strain rate tensile (SSRT) test. Generally, plastic prestrain reduces the
SCC resistance in various welded zones. The SCC susceptibility of the test materials can be put in the following order: heat-affected
zone (HAZ) > weld metal (WM) > base metal (BM). Fractographic analysis indicates that there are two cracking modes, mode I
and mode II, during SSRT tests. Mode I cracks propagate along the direction perpendicular to the maximum tensile stress, and
mode II cracks lie in planes roughly parallel to the plane where the maximum shear exists. The SCC of the BM is governed by
mode I cracking and fracture of the HAZ, and the WM is dominated by mode II cracking. Damage analysis shows that the detrimental
impact of plastic prestrain on the residual SCC resistance cannot be evaluated with the linear superposition model. A plastic
prestrain sensitivity, a material constant independent of plastic prestrain, is proposed to characterize the susceptibility
of SCC resistance to plastic prestrain, and it increases with the SCC susceptibility of the steels. The enhanced SCC susceptibility
caused by plastic prestrain may be related to an increase in yield strength. The correlation of the ratio of the reduction
in area in NS4 solution to that in air (RA
SCC/RA
air) with the yield strength is microstructure dependent. |
| |