Fabrication of CoZn alloy nanowire arrays: Significant improvement in magnetic properties by annealing process |
| |
Authors: | M. KoohborS. Soltanian M. Najafi P. Servati |
| |
Affiliation: | a Department of Physics, University of Kurdistan, Sanandaj, Iran b Department of Physics, Hamadan University of Technology, Hamadan, Iran c Department of Electrical and Computer Engineering, University of British Columbia, Vancouver, Canada |
| |
Abstract: | Highly ordered arrays of Co1−xZnx (0 ≤ x ≤ 0.74) nanowires (NWs) with diameters of ∼35 nm and high length-to-diameter ratios (up to 150) were fabricated by co-electrodeposition of Co and Zn into pores of anodized aluminum oxide (AAO) templates. The Co and Zn contents of the NWs were adjusted by varying the ratio of Zn and Co ion concentrations in the electrolyte. The effect of the Zn content, electrodeposition conditions (frequency and pH) and annealing on the structural and magnetic properties (e.g., coercivity (Hc) and squareness (Sq)) of NW arrays were investigated using X-ray diffraction (XRD), scanning electron microscopy, electron diffraction, and alternating gradient force magnetometer (AGFM). XRD patterns reveal that an increase in the concentration of Zn ions of the electrolyte forces the hcp crystal structure of Co NWs to change into an amorphous phase, resulting in a significant reduction in Hc. It was found that the magnetic properties of NWs can be significantly improved by appropriate annealing process. The highest values for Hc (2050 Oe) and Sq (0.98) were obtained for NWs electrodeposited using 0.95/0.05 Co:Zn concentrations at 200 Hz and annealed at 575 °C. While the pH of electrolyte is found to have no significant effect on the structural and magnetic properties of the NW arrays, the electrodeposition frequency has considerable effects on the magnetic properties of the NW arrays. The changes in magnetic property of NWs are rooted in a competition between shape anisotropy and magnetocrystalline anisotropy in NWs. |
| |
Keywords: | Electrodeposition CoZn nanowire arrays Magnetic properties AAO template |
本文献已被 ScienceDirect 等数据库收录! |
|