Separation efficiency of alumina particles in Al melt under high frequency magnetic field |
| |
| Authors: | GUO Qing-tao CAO Zhi-qiang ZHANG Zhong-tao LI Ting-ju JIN Jun-z e HONG Chun-pyo Center for Computer-Aided Solidification Processing Metallurgical System Engineering Yonsei University Seoul Korea School of Materials Science Engineering Dal ian University of Technology Dalian China |
| |
| Affiliation: | [1]Center for Computer-Aided Solidification Processing, Metallurgical System Engineering, Yonsei University, Seoul 120749, Korea; [2]School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, China |
| |
| Abstract: | The effects of separation time and magnetic induction intensity on the separation efficiency of alumina particles with diameters varying from 30 to 200 μm in aluminum melt were investigated. The experimental results show that the particle-accumulated layer is formed in the periphery of the solidified specimen when the diameter of the separated molten metal, the magnetic induction intensity and the separation time are 10 mm, 0.04 T and 1 s, respectively. When the separation time is 2 s, the particle-accumulated layer can be observed obviously and the separation efficiency is about 80%. There are few alumina particles in the inner of the solidified specimen when the separation time is 3 s. The separation efficiency higher than 85% can be achieved when the separation time is longer than 3 s. When the magnetic induction intensity is 0.06 T, the visible particle-accumulated layer can be formed in 1 s and the separation efficiency is higher than 95%. The experimental results were compared with the calculated results at last. |
| |
| Keywords: | Al melt alumina particles electromagnetic separation high frequency magnetic field separation efficiency |
| 本文献已被 CNKI 维普 万方数据 ScienceDirect 等数据库收录！ |