| 转炉渣系矿物相研究 |
| |
| 引用本文： | 邓志豪,王珏,周云.转炉渣系矿物相研究[J].安徽工业大学学报,2011(3):201-204. |
| |
| 作者姓名： | 邓志豪 王珏 周云 |
| |
| 作者单位： | 安徽工业大学冶金与资源学院; |
| |
| 摘 要： | 分析不同转炉渣的化学组成,结合国内某钢铁厂风碎渣的成份,选择以CaO-MgO-SiO2-Fe2O3四元渣系作为基础渣,质量分数分别为48%,10%,12%和30%,将它作为实验室的合成渣系.使用SEM及EDS对各渣样矿物相进行分析,结果表明:该渣系矿物相的结构、组成与原渣的非常相近,即固溶了少量Fe元素的黑色f-MgO...
|
| 关 键 词： | 转炉渣 合成渣 矿物相 分析纯剂 |
Study on the Mineral Phase of the Converter Slag System |
| |
| DENG Zhi-hao,WANG Jue,ZHOU Yun.Study on the Mineral Phase of the Converter Slag System[J].Journal of Anhui University of Technology,2011(3):201-204. |
| |
| Authors: | DENG Zhi-hao WANG Jue ZHOU Yun |
| |
| Affiliation: | DENG Zhi-hao,WANG Jue,ZHOU Yun(School of Metallurgy & Resources,Anhui University of Technology,Ma'anshan 243002,China) |
| |
| Abstract: | Quaternary slag system of CaO-MgO-SiO2-Fe2O3 has been synthetized as object of the experiment of modification,the chemical content of the synthetic slag was CaO-48%,MgO-10%,SiO2-12%Fe2O3-30%,respectively.The mineral phase of the slag samples were analyzed by SEM and EDS,the results showed that the microstruction and mineral composition of phase of synthetized slag was very similar with the wind-crushing slag,where f-MgO with a small amount of Fe element dissolution presented black;2CaO?SiO2] phase presente... |
| |
| Keywords: | converter slag synthetic slag mineral phase AR agent |