Effect of Titania Additive on Structural and Mechanical Properties of Alumina–Fluorapatite Composites

Mechanical properties of alumina-fluorapatite composites with different titania additive amounts (0, 0.5, 1, 1.4, 2, 3, 4 and 5 wt%) have been investigated between 1200 and 1600℃. The optimum values of densification and mechanical properties of composites have been reached with 1.4 wt% of titania after the sintering process at 1500℃ for 1 h. Thus, the rupture strength of alumina-26.52 wt% Fap-1.4 wt% TiO2 reaches 75 MPa. At higher temperature and beyond 1.4 wt% TiO2 ,the densification and mechanical properties were hindered by the formation of both intergranular porosity and secondary phase. X-ray diffraction (XRD) analysis of alumina-Fap-TiO2 composites shows the formation of aluminium titanate (Al2O3-TiO2:Al2TiO5 ). The 27Al magic angle scanning nuclear magnetic resonance analysis of Al2O3-Fap-TiO2 composites reveals the presence of octahedral and pentahedral aluminium and novel environment relative to tetrahedral aluminium sites.