Chemical reduction of nanocrystalline CeO2

The reduction of commercial and mechanochemically processed CeO₂ powders was studied. Nanostructured CeO₂, with the crystallite size of 21 nm and the lattice distortion of 0.37%, was obtained during 60 min of milling in a high-energetic vibratory mill. X-ray diffraction, scanning electron microscopy and Brunauer-Emmett-Teller method were applied to characterize the milled powders. During the thermal treatment at 1200 and 1400 °C in an argon atmosphere the nonstoichiometric CeO_2−x oxides with the defect fluorite structure were formed. Compositions of CeO_2−x oxides were determined according to its lattice parameter. The results showed that the release of oxygen, as well as the rate of reduction, was more effective in nanocrystalline then in the microcrystalline CeO₂, producing at 1200 °C CeO_1.80 and CeO_1.85 oxides, while at 1400 °C were obtained similarly, CeO_1.77 and CeO_1.78, compositions.