Microwave Dielectric Properties of Li2TiO3 Ceramics Doped with ZnO–B2O3 Frit

A type of new low sintering temperature ceramic, Li₂TiO₃ ceramic, has been found. Although it is difficult for the Li₂TiO₃ compound to be sintered compactly at temperatures above 1000°C for the volatilization of Li₂O, dense Li₂TiO₃ ceramics were obtained by conventional solid-state reaction method at the sintering temperature of 900°C with the addition of ZnO–B₂O₃ frit. The sintering behavior and microwave dielectric properties of Li₂TiO₃ ceramics with less ZnO–B₂O₃ frit (≤3.0 wt%) doping were investigated. The addition of ZnO–B₂O₃ frit can lower the sintering temperature of the Li₂TiO₃ ceramics, but it does not apparently degrade the microwave dielectric properties of the Li₂TiO₃ ceramics. Typically, the good microwave dielectric properties of ɛ_r=23.06, Q × f =32 275 GHz, τ_f = 35.79 ppm/°C were obtained for 2.5 wt% ZnO–B₂O₃ frit-doped Li₂TiO₃ ceramics sintered at 900°C for 2 h. The porosity was 0.08%. The Li₂TiO₃ ceramic system may be a promising candidate for low-temperature cofired ceramics applications.