Sinterability and properties of Ti(N1−x,O x ) y -(V,Ta)C-Ni sintered alloys having a golden colour

The effect of oxygen and carbide addition on the sinterability of TiN_y(0.42<y<1)-Ni alloys, in which part of the nitrogen is replaced by oxygen was investigated. It was found that sinterability increased as the oxygen and carbide content increased, but the strength of the resultant sintered alloys was significantly reduced due to the presence of Ni₃Ti and Ti₂O₃ phases when the oxygen content exceeded 50 mol %. The sintered alloy with the highest hardness was found whenx=0.7,y=0.78 and the (V,Ta)C content was 18% by weight and this alloy was characterized by having a low density, good corrosion resistance and the colour of gold.