| Influence of Initial Microstructure on the Strengthening Effect of Extruded Mg–8Sn–4Zn–2Al Alloys |
| |
| 摘 要： | The Mg–8Sn–4Zn–2Al(TZA842, in wt%) alloys with different initial microstructure(as-cast-AC and homogenization treatment-HT) subjected to hot extrusion. Also, the strengthening responses to AC and HT for the extruded TZA842 alloys were reported. The results revealed that the alloy subjected to HT shows finer grain size, more homogenous microstructure and weaker basal texture than those of counterpart subjected to AC. In addition, compared with TZA842-AC alloy, precipitates were finer and uniformly dispersed in TZA842-HT owing to the utilization of HT. Moreover, the TZA842-HT alloy showed higher yield strength of 200 MPa, ultimate tensile strength of 290 MPa and elongation(EL) of17.9% than those of TZA842-AC, which was mainly attributed to the combined effects of grain boundary strengthening,precipitation strengthening, solid solution strengthening and weak texture. Strengthening mechanism for both alloys was discussed in detail.
|
| 收稿时间： | 2017-08-24 |
Influence of Initial Microstructure on the Strengthening Effect of Extruded Mg-8Sn-4Zn-2Al Alloys |
| |
| Yang Bai,Wei-Li Cheng,Shi-Chao Ma,Jun Zhang,Chen Guo,Yao Zhang. Influence of Initial Microstructure on the Strengthening Effect of Extruded Mg-8Sn-4Zn-2Al Alloys[J]. Acta Metallurgica Sinica(English Letters), 2018, 31(5): 487. DOI: 10.1007/s40195-017-0673-5 |
| |
| Authors: | Yang Bai Wei-Li Cheng Shi-Chao Ma Jun Zhang Chen Guo Yao Zhang |
| |
| Affiliation: | 1.School of Materials Science and Engineering Taiyuan University of Technology Taiyuan China2.Shanxi Key Laboratory of Advanced Magnesium-Based Materials Taiyuan University of Technology Taiyuan China3.Key Laboratory of Interface Science and Engineering in Advanced Materials, Ministry of Education Taiyuan University of Technology Taiyuan China |
| |
| Abstract: | The Mg-8Sn-4Zn-2Al (TZA842, in wt%) alloys with different initial microstructure (as-cast-AC and homogenization treatment-HT) subjected to hot extrusion. Also, the strengthening responses to AC and HT for the extruded TZA842 alloys were reported. The results revealed that the alloy subjected to HT shows finer grain size, more homogenous microstructure and weaker basal texture than those of counterpart subjected to AC. In addition, compared with TZA842-AC alloy, precipitates were finer and uniformly dispersed in TZA842-HT owing to the utilization of HT. Moreover, the TZA842-HT alloy showed higher yield strength of 200 MPa, ultimate tensile strength of 290 MPa and elongation (EL) of 17.9% than those of TZA842-AC, which was mainly attributed to the combined effects of grain boundary strengthening, precipitation strengthening, solid solution strengthening and weak texture. Strengthening mechanism for both alloys was discussed in detail. |
| |
| Keywords: | Mg-Sn alloy Extrusion Microstructure Tensile property Strengthening mechanism |