Effects of Octahedral Tilting on the Piezoelectric Properties of Strontium/Barium/Niobium-Doped Soft Lead Zirconate Titanate Ceramics

(Pb_1?x?ySr_xBa_y)(Zr_0.976?zTi_zNb_0.024)O₃ solid solutions have been investigated to understand the relationship between structural changes caused by isovalent strontium and barium substitution on the A-site and dielectric and piezoelectric properties. As strontium and barium were substituted for lead, the zirconium:titanium (Zr:Ti) ratio was modified so that all compositions had an optimized piezoelectric coefficient (d₃₃). The value of d₃₃ was at a maximum in the tetragonal phase near, but not at, the morphotropic-phase boundary (MPB). The real MPB was taken as the Zr:Ti ratio at which X-ray diffraction patterns appeared either pseudocubic or a mixture of rhombohedral and tetragonal. As strontium content increased, optimized d₃₃ also increased from 410 pC/N (x= 0) to 640 pC/N (x= 0.12), commensurate with a decrease in the paraelectric-to-ferroelectric phase transition temperature (T_C) from 350°C (x= 0) to 175°C (x= 0.12). However, for ceramics where x > 0.12, optimized d₃₃ decreased even though the phase-transition temperature was ～150°C. Low strontium concentration ceramics (x= 0–0.08) contained 80 nm ferrroelectric domains typical of PZT, but high strontium concentration ceramics (x= 0.12–0.16) contained fine-scale domains (20 nm) in some regions of the microstructure. In addition, 110] pseudocubic electron diffraction patterns revealed superlattice reflections at 1/2{hkl} positions associated with rotations of the octahedra in antiphase. Co-doping ceramics with strontium (x= 0.06) and barium (y= 0.06) resulted in the disappearance of the 1/2{hkl} reflections. Optimized d₃₃ (～520 pC/N, T_C～ 205°C) for this composition was similar to that of ceramics where x= 0.08, y= 0, which had a T_C of ～250°C.