An XPS study of anodic behavior of amorphous nickel-phosphorus alloys containing chromium,molybdenum or tungsten in 1 m CHl

The surfaces of amorphous Ni-18P, Ni-IOCr-20P, Ni-9Mo-19P and Ni-5W-18P alloys immersed or anodically polarized in 1 M HCl solution were analyzed in connection with their corrosion and anodic behavior. All alloys were more corrosion-resistant than crystalline nickel metal because of formation of phosphate-containing surface films on the Ni-18P, Ni-9Mo-19P and Ni-5W-18P alloys and because of spontaneous passivation due to formation of passive hydrated chromium oxyhydroxide film on the Ni-10Cr-20P alloy. The latter alloy was stable up to the transpassive region of chromium although intrusion of phosphate in the film was responsible for the higher passive current density in comparison to the amorphous Fe-Cr-13P-7C alloy of the same chromium content. The formation of thick porous phosphate films containing nickel, and molybdenum or tungsten by anodic polarization was not effective in passivating the Ni-18P, Ni-9Mo-19P and Ni-5W-18P alloys, and they suffered pitting corrosion by anodic polarization.