Influence of Surface Stress on indentation Cracking |
| |
Authors: | D. J. GREEN B. R. MALONEY |
| |
Affiliation: | Department of Materials Science and Engineering, The Pennsylvania Stave University, University Park, Pennsylvania 16802 |
| |
Abstract: | A simple, two-dimensional fracture mechanics analysis was used to determine the influence of nonuniform residual surface stresses on the formation of radial indentation cracks. The indentation behavior depends on the depth of the compressive stresses, such that the apparent fracture toughness passes through a maximum with increasing indentation load. The analysis was used to estimate the surface stress from indentation data for a zirconia-toughened ceramic and was compared to previous X-ray diffraction measurements of this stress. The comparison gives only fair agreement; the sources of possible error are discussed. Such surface stresses also influence the accuracy of K I C measurements when an indentation crack length technique is used; surface preparation is a critical factor in the measurement. Finally, the K I C values obtained from indentation crack sizes were compared with those obtained by the double-cantilever-beam technique. |
| |
Keywords: | |
|
|