Extraction of Vanadium from LD Converter Slag by Pressure Leaching Process with Titanium White Waste Acid |
| |
Affiliation: | Key Laboratory of Ecological Utilization of Multi-metal Intergrown Ores of Ministry of Education, Northeastern University, Shenyang 110819, China |
| |
Abstract: | The process of extraction vanadium from LD converter slag by pressure leaching with titanium white waste acid was investigated. The mineralogy analysis indicates that several kinds of spinel containing Fe, V, Ti, Mn and Cr, mainly exist in the converter slag. Potential-pH diagrams of V-Fe-H2O, V-Ti-H2O, V-Mn-H2O, V-Cr-H2O system have been calculated at elevated temperature condition (150 oC). The thermodynamics diagrams show that soluble ions of V and Fe2+, Fe3+, Mn2+, Cr2+ and Cr3+ can be extracted by the acidic leachate during the pressure leaching process. The results of orthogonal experiment reveal that the impacts of temperature and initial acid concentration on the vanadium extraction process are effective. The effect of temperature on the leaching process was further investigated with a increased temperature from 100 oC to 160 oC, and the results indicate that the content of titanium in the residue is 4.56% to about 12.0%, while other elements tend to be enriched in the leaching solution. Under the optimization condition (temperature 140 oC, liquid-solid ratio 10:1, concentration of acid at 200 g·L-1, stirring speed 500 r/min and the reaction time of 90 min), the leaching rate of vanadium is 96.85% |
| |
Keywords: | extraction vanadium titanium white waste acid LD converter slag pressure leaching potential-pH diagrams |
|
| 点击此处可从《稀有金属材料与工程》浏览原始摘要信息 |
|
点击此处可从《稀有金属材料与工程》下载全文 |
|