Damage mechanism in weldment of 2.25Cr-1Mo steel under creep-fatigue loading

The purpose of this study is to clarify damage process of “Type IV cracking” in weldment of a 2.25Cr-1Mo steel and to propose a micro damage prediction method. From continuous observation under a creep-fatigue test, it was found that spherical shape voids initiated and grew on grain boundaries in fine grain region and these voids grow continuously by changing their shape to crack-like. Both spherical and crack-like void growth rate equations were derived from the proposed void growth model. It was indicated that measured void growth rate under the creep-fatigue loading was well predicted by the growth rate equations.