Mechanism of Alumina-Enhanced Sintering of Fine Zirconia Powder: Influence of Alumina Concentration on the Initial Stage Sintering

The isothermal shrinkage behavior of 2.9 mol% Y₂O₃-doped ZrO₂ powders with 0–1 mass% Al₂O₃ was investigated to clarify the effect of Al₂O₃ concentration on the initial sintering stage. The shrinkage of the powder compact was measured at constant temperatures in the range of 950°–1050°C. The Al₂O₃ addition increased the densification rate with increasing temperature. The values of apparent activation energy ( nQ ) and apparent frequency-factor term (β₀ ⁿ ), where n is the order depending on the diffusion mechanism, were estimated at the initial sintering stage by applying a sintering-rate equation to the isothermal shrinkage data. The diffusion mechanism changed from grain-boundary diffusion (GBD) to volume diffusion (VD) by Al₂O₃ addition and both nQ and β₀ ⁿ increased with increasing Al₂O₃ concentration. The kinetic analysis of the sintering mechanism suggested that the increase of densification rate by Al₂O₃ addition largely depends on the increase of β₀ ⁿ , that is, the increases of n with GBD→VD change and β₀ with an increase in Al₂O₃ content, although the nQ also increases with Al₂O₃ addition. This enhanced sintering mechanism is reasonably interpreted by the segregated dissolution of Al₂O₃ at ZrO₂ grain boundaries.