Processing and Properties of TiB2 with MoSi2 Sinter-additive: A First Report

The densification of non-oxide ceramics like titanium boride (TiB₂) has always been a major challenge. The use of metallic binders to obtain a high density in liquid phase-sintered borides is investigated and reported. However, a non-metallic sintering additive needs to be used to obtain dense borides for high-temperature applications. This contribution, for the first time, reports the sintering, microstructure, and properties of TiB₂ materials densified using a MoSi₂ sinter-additive. The densification experiments were carried out using a hot-pressing and pressureless sintering route. The binderless densification of monolithic TiB₂ to 98% theoretical density with 2–5 μm grain size was achieved by hot pressing at 1800°C for 1 h in vacuum. The addition of 10–20 wt% MoSi₂ enables us to achieve 97%–99%ρ_th in the composites at 1700°C under similar hot-pressing conditions. The densification mechanism is dominated by liquid-phase sintering in the presence of TiSi₂. In the pressureless sintering route, a maximum of 90%ρ_th is achieved after sintering at 1900°C for 2 h in an (Ar+H₂) atmosphere. The hot-pressed TiB₂–10 wt% MoSi₂ composites exhibit high Vickers hardness (～26–27 GPa) and modest indentation toughness (～4–5 MPa·m^1/2).