| 成型压力对氧化铝瓷球性能的影响 |
| |
| 引用本文： | 颜东亮,吴伯麟,钟莲云. 成型压力对氧化铝瓷球性能的影响[J]. 佛山陶瓷, 2004, 14(5): 10-12 |
| |
| 作者姓名： | 颜东亮 吴伯麟 钟莲云 |
| |
| 作者单位： | 桂林工学院,541004;桂林工学院,541004;桂林工学院,541004 |
| |
| 摘 要： | 研究了成型压力对瓷球烧结、密度及耐磨性的影响。结果表明：在本研究系统内随着压力的增加，瓷球的烧结温度下降，烧成温度范围拓宽。采用150MPa成型的瓷球的密度最大且耐磨性最好。
|
| 关 键 词： | 成型压力 等静压成型 氧化铝瓷球 耐磨性 烧成温度范围 |
Influence on Behaviour of Alumina Ball by Using Different Forming Pressure |
| |
| Yan Dongliang Wu Bolin Zhong Lianyun. Influence on Behaviour of Alumina Ball by Using Different Forming Pressure[J]. Foshan Ceramics, 2004, 14(5): 10-12 |
| |
| Authors: | Yan Dongliang Wu Bolin Zhong Lianyun |
| |
| Affiliation: | Guilin college of Technology 541004 |
| |
| Abstract: | The influence of different forming pressure on isostatic alumina ball sintering,density and wear resistance have been investigated,adopting the pressure of 50MPa,100MPa,150MPa,200MPa,250MPa and 300MPa to produce ball.The result shows that the ball sintering temperature decreases,while sintering temperature range enlarges with the pressure increase;the highest density and the lowest wear rate is obtained at the pressure of 100MPa. |
| |
| Keywords: | forming pressure isostatic pressing alumina ball wear resistance sintering temperature range |