Precipitation and evolution of nodular graphite during solidification process of ductile iron |
| |
Authors: | Liu Jin-hai Yan Jian-shuai Zhao Xue-bo Fu Bin-guo Xue Hai-tao Zhang Gui-xian Yang Peng-hui |
| |
Affiliation: | 1.School of Materials Science and Engineering, Hebei University of Technology, Tianjin, 300130, China ;2.Key Laboratory of Research and Application of Mould Materials for Glass and Rubber in Hebei Province, Huanghua, 061000, China ;3.Hebei Andi Mould Co., Ltd, Huanghua, 061000, China ;4.School of Materials Science and Engineering, Beijing University of Technology, Beijing, 100124, China ; |
| |
Abstract: | The quantity and morphology of spheroidal graphite have an important effect on the properties of ductile iron,and the characteristics of spheroidal graphite are determined by the solidification process.The aim of this work is to explore the precipitation and evolution of graphite nodules in hypoeutectic,eutectic,and hypereutectic ductile irons by thermal analysis,liquid quenching and metallographic technique.Results show that hypoeutectic ductile iron has the longest solidification time and the lowest eutectic temperature;eutectic ductile iron has the shortest solidification time;hypereutectic ductile iron has the highest eutectic temperature.After solidification is completed,hypoeutectic ductile iron has the lowest nodule count,nodularity and graphite fraction;eutectic ductile iron has the highest nodule count,nodularity and the smallest nodule diameter;hypereutectic has the highest nodule diameter and graphite fraction.The nucleation and growth of graphite nodules in hypereutectic ductile iron starts before bulk eutectic crystallization stage,however,the precipitation and evolution of graphite nodules of hypoeutectic and eutectic ductile irons mainly occur in the eutectic crystallization stage.The graphite precipitated in eutectic crystallization of hypoeutectic,eutectic,and hypereutectic ductile irons,are 61%,68% and 43% of total graphite volume fraction,respectively.Simultaneously,there are plenty of austenite dendrites in hypoeutectic and hypereutectic ductile irons,which are prone to shrinkage defects.Therefore,the eutectic ductile iron has the smallest shrinkage tendency. |
| |
Keywords: | |
本文献已被 CNKI SpringerLink 等数据库收录! |
|