Flow stress behavior of Al-Cu-Li-Zr alloy containing Sc during hot compression deformation |
| |
Authors: | Wen-jie Liang Qing-lin Pan Yun-bin He Yun-chun Li and Xiao-gang Zhang |
| |
Affiliation: | [1]School of Materials Science and Engineering,Central South University,Changsha 410083,China [2]School of Chemistry and Chemical Engineering,Central South University,Changsha 410083,China |
| |
Abstract: | The flow stress behavior of A1-3.5Cu-1.5Li-0.25(Sc Zr) alloy during hot compression deformation was studied by isothermal compression test using Gleeble-1500 thermal-mechanical simulator. Compression tests were preformed in the temperature range of 653-773K and in the strain rate range of 0.001-10s-1 up to a tree plastic strain of 0.7. The results indicate that the flow stress of the alloy increases with increasing strain rate at a given temperature, and decreases with increasing temperature at a given imposed strain rate. The relationship between the flow stress and the strain rate and the temperature was derived by analyzing the experimental data. The flow stress is in a hyperbolic sine relationship with the strain rate, and in an Arrhenius relationship with the temperature, which imply that the process of plastic deformation at an elevated temperature for this material is thermally activated. The flow stress of the alloy during the elevated temperature deformation can be represented by a Zener-Hollomon parameter with the inclusion of the Arrhenius term. The values of n, a and A in the analytical expressions of flow stress σ are fitted to be 5.62, 0.019MPa-1 and 1.51×1016s-1, respectively. The hot deformation activation energy is 240.85kJ/mol. |
| |
Keywords: | AI-Cu-Li-Zr alloy containing Sc flow stress hot compression deformation Zener-Hollomon parameter |
本文献已被 维普 万方数据 SpringerLink 等数据库收录! |
|