Single pass laser joining of Inconel 718 superalloy with filler

Abstract

Microstructure and mechanical property of CO₂ laser beam welded IN 718 superalloy were studied by electron microscopy and hardness testing. The use of a welding filler wire produced a sound fusion zone with no cracking but grain boundary microfissuring occurred in the heat affected zone (HAZ) and was observed to be significantly influenced by pre-weld heat treatment and laser welding speed. Crack-free weld was produced by a pre-weld heat treatment that minimised non-equilibirum grain boundary boron segregation and inhibited grain growth. While post-weld heat treatment (PWHT) reduced the difference between the hardness values of the base alloy, HAZ and the fusion zone, it resulted in increased HAZ cracking, which was likely aided by pre-existing cracks. The PWHT cracking was, however, avoided by subjecting pre-weld material to the heat treatment condition that produces crack-free weld during welding process.