Sulphur segregation and precipitation in HAZ of boiler steel thick section welds

Abstract

Stress relief cracking can occur in weld heat affected zones (HAZ) after post-weld heat treatment (PWHT) and periods of service at elevated temperatures. Stress relief cracking is generally believed to occur by sulphur induced decohesion ahead of a growing sharp crack. The impurity segregation behaviour in a microalloyed steel, typical of that used in the construction of a power station boiler where intermittent cracks were observed along the weld fusion boundaries, has been assessed. In particular the type and amount of segregation in the coarse grained HAZ (CGHAZ) before and after PWHT has been determined. It was found that significant sulphur segregation occurred during the CGHAZ thermal cycle resulting in elemental sulphur on the prior austenite grain boundaries. Following PWHT some desegregation of sulphur, coupled with the formation of sulphides and carbides on the prior austenite grain boundaries, was observed; in addition, significant phosphorus segregation to the prior austenite grain boundaries and grain boundary precipitate/matrix interfaces was seen.