| 不同的预先热处理对T10钢低温盐浴渗铬的影响 |
| |
| 引用本文： | 叶金玲,邹敢锋,于小勇.不同的预先热处理对T10钢低温盐浴渗铬的影响[J].热加工工艺,2003(6):33-34. |
| |
| 作者姓名： | 叶金玲 邹敢锋 于小勇 |
| |
| 作者单位： | 华南理工大学,机械学院,广东,广州,510641 |
| |
| 摘 要： | 研究了不同的预先热处理对T10钢低温盐浴渗铬的影响。结果表明，经离子渗氮后再进行低温盐浴渗铬，在同样的渗铬工艺条件下，其渗层深度增加最多。
|
| 关 键 词： | 离子渗氮 低温渗铬 |
| 文章编号： | 1001-3814(2003)06-0033-02 |
| 修稿时间： | 2003年3月17日 |
Influence of Different Pre-heattreatment on Low Temperature Salt-bath Chromizing of T10 Steel |
| |
| YE Jin-ling,ZOU Gan-feng,YU Xiao-yong.Influence of Different Pre-heattreatment on Low Temperature Salt-bath Chromizing of T10 Steel[J].Hot Working Technology,2003(6):33-34. |
| |
| Authors: | YE Jin-ling ZOU Gan-feng YU Xiao-yong |
| |
| Abstract: | Influence of different pre-heattreatment on low temperature salt-bath chromizing of T10 steel was studied . The results show that the T10 steel is chromized under the low temperature salt-bath after being ionicnitrided ,the depth of chromized layer increase the most under the same condition . |
| |
| Keywords: | ionitriding low temperature chromizing |