| 薄板铝铜搭接搅拌摩擦焊工艺 |
| |
| 引用本文： | 张骁,王敏,张会杰,朱智,于涛,吴振强.薄板铝铜搭接搅拌摩擦焊工艺[J].精密成形工程,2017,9(5):187-191. |
| |
| 作者姓名： | 张骁 王敏 张会杰 朱智 于涛 吴振强 |
| |
| 作者单位： | 中国科学院沈阳自动化研究所，沈阳 110016,中国科学院沈阳自动化研究所，沈阳 110016,中国科学院沈阳自动化研究所，沈阳 110016,中国科学院沈阳自动化研究所，沈阳 110016,中国科学院沈阳自动化研究所，沈阳 110016,中国科学院沈阳自动化研究所，沈阳 110016 |
| |
| 基金项目： | 国家自然科学基金（51505471） |
| |
| 摘 要： | 目的研究铝铜异种材料的搅拌摩擦焊搭接工艺,揭示搭接接头界面行为演变的基本规律。方法对1mm的6061铝合金与1 mm的紫铜薄板进行搅拌摩擦焊搭接焊接,测试焊缝的力学性能,对焊缝组织进行分析。结果焊缝表面成形良好,焊缝内部无缺陷。接头的最高拉伸强度达到1447 N,观察拉伸接头断口形貌,发现断裂均发生在上层铝合金的热影响区。结论接头连接界面区域生成钩状"自锁紧"结构,这种钩状"自锁紧"结构增加了铝铜之间的有效接触面积,有利于提高焊缝连接强度。
|
| 关 键 词： | 搅拌摩擦焊 薄板 铝铜 搭接 自锁紧 |
| 收稿时间： | 2017/6/29 0:00:00 |
| 修稿时间： | 2017/9/10 0:00:00 |
Friction Stir Welding Process for Lap Joint of Aluminum Copper Sheet |
| |
| ZHANG Xiao,WANG Min,ZHANG Hui-jie,ZHU Zhi,YU Tao and WU Zhen-qiang.Friction Stir Welding Process for Lap Joint of Aluminum Copper Sheet[J].Journal of Netshape Forming Engineering,2017,9(5):187-191. |
| |
| Authors: | ZHANG Xiao WANG Min ZHANG Hui-jie ZHU Zhi YU Tao and WU Zhen-qiang |
| |
| Affiliation: | Shenyang Institute of Automation, Chinese Academy of Science, Shenyang 110016, China,Shenyang Institute of Automation, Chinese Academy of Science, Shenyang 110016, China,Shenyang Institute of Automation, Chinese Academy of Science, Shenyang 110016, China,Shenyang Institute of Automation, Chinese Academy of Science, Shenyang 110016, China,Shenyang Institute of Automation, Chinese Academy of Science, Shenyang 110016, China and Shenyang Institute of Automation, Chinese Academy of Science, Shenyang 110016, China |
| |
| Abstract: | The paper aims to study the friction stir welding process for lap joint of aluminum-copper sheet and reveal the basic law in interfacial behavior evolution of lap joint. Friction stir welding was carried out on 1 mm of 6061 aluminum-copper sheet to test mechanical properties of the weld and analyze weld microstructure. The weld surface looked well and there was no defect inside the weld. The maximum tensile strength of the joint reached 1447 N. By observing the tensile fracture morphology, fracture was found to occur in the heat affected zone of upper aluminum alloy. Self-locking structure is formed in the connection interface area of joint. Such structure increases the effective contact area between aluminum and copper and improves the strength of weld joint. |
| |
| Keywords: | friction stir welding sheet Al-Cu lap joint self-locking |