Abrasive wear of Al2O3-reinforced aluminium-based MMCs

The effects of volume fraction, Al₂O₃ particle size and effects of porosity in the composites on the abrasive wear resistance of compo-casting Al alloy MMCs have been studied for different abrasive conditions. It was seen that porosity in the composites is proportional to particle content. In addition, process variables like the stirring speed, and the position and diameter of the stirrer affect of the porosity content in a way similar to that observed for particle content. In addition, the abrasive wear rates of composites decreased more rapidly with increase in Al₂O₃ volume fraction in tests performed over 80 grade SiC abrasive paper than in tests conducted over 220 grade SiC abrasive paper. Furthermore, the wear rates decreased with increase in Al₂O₃ size for the composites containing the same amount of Al₂O₃. Hence, it is deduced that aluminium alloy composites reinforced with larger Al₂O₃ particles are more effective against abrasive wear than those reinforced with smaller Al₂O₃ particles. At the same time the results show that the beneficial effects of hard Al₂O₃ particles on wear resistance far surpassed that of the sintered porosity in the compocasting metal-matrix composites (MMCs). Nevertheless, the fabrication of composites containing soft particles such as graphite favors a reduction in the friction coefficient. For this reason graphite and copper were used in the matrix in different amounts to detect their effect on wear resistance. Finally, it was seen that wear rate of the composites decreased considerably with graphite additions.