Preparation and characterization of LaFe1−xMgxO3/Al2O3/FeCrAl: Catalytic properties in methane combustion

MnO_x–CeO₂ mixed oxides prepared by sol–gel method, coprecipitation method and modified coprecipitation method were investigated for the complete oxidation of formaldehyde. Structure analysis by H₂-TPR and XPS revealed that there were more Mn⁴⁺ species and richer lattice oxygen on the surface of the catalyst prepared by the modified coprecipitation method than those of the catalysts prepared by sol–gel and coprecipitation methods, resulting in much higher catalytic activity toward complete oxidation of formaldehyde. The effect of calcination temperature on the structural features and catalytic behavior of the MnO_x–CeO₂ mixed oxides prepared by the modified coprecipitation was further examined, and the catalyst calcined at 773 K showed 100% formaldehyde conversion at a temperature as low as 373 K. For the samples calcined below 773 K, no any diffraction peak corresponding to manganese oxides could be detected by XRD measurement due to the formation of MnO_x–CeO₂ solid solution. While the diffraction peaks corresponding to MnO₂ phase in the samples calcined above 773 K were clearly observed, indicating the occurrence of phase segregation between MnO₂ and CeO₂. Accordingly, it was supposed that the strong interaction between MnO_x and CeO₂, which depends on the preparation route and the calcination temperature, played a crucial role in determining the catalytic activity toward the complete oxidation of formaldehyde.