Factors Affecting the Coercivity and Remanence of Artificial Magnetite

Abstract

Sintered chemically pure ferric oxide particles were reduced by a mixture of carbon monoxide and carbon dioxide in a rotary drum furnace. The product was then concentrated in a Davis tube and from the hysteresis loop of the minus 65 plus 100 mesh particles of the magnetics, the volume average remanence and coercivity were obtained.

It was found that the residual magnetism and coercive force of the particles were inversely proportional to the reduction temperature. Reduction time had no significant effect on either coercive force or residual magnetism.

Résumé

Des particules d'oxyde ferrique aggloméré, chimiquement pur, ont été réduites par un mélange de monoxyde de carbone et bioxyde de carbone dans un four à tambour rotatif. Le produit fut ensuite concentré dans un tube Davis, et la rémanence moyenne par volume ainsi que la coercivité furent obtenues du cycle d'hystérésis des particules entre 65 et 100 mailles de la fraction magnétique.

On trouva que la magnétisme residuel et la force coercive des particules étaient inversement proportionnels à la température de réduction. La durée de la réduction n'avait guère d'effet sur la force coercive ou Ie magnétisme résiduel.