Intercritical Deformation of Low Carbon Steel |
| |
Abstract: | AbstractImproving the strength of steel sheets by increasing the carbon content decreases the formability and highly impairs the weldability. Thermomechanical processing (TMP) is one of the most important mechanisms that simultaneously enhances the strength and ductility while keeping the excellent weldability of low carbon steel. The influence of TMP in the (α + γ) region on the microstructure and mechanical properties of low carbon steel (LC) is investigated. The TMP was carried out by rolling at 760, 810 and 860 C with different amounts of reductions followed by water quenching. Rolling was maintained at 5 m/min rolling speed. The results showed that high strength with good elongation was obtained using intercritical deformation at both 810 °C and 70% total rolling reduction.L’amélioration de la résistance mécanique des feuilles d’acier par augmentation du contenu en carbone diminue la formabilité et affecte beaucoup la soudabilité. Le traitement thermomécanique (TMP) est l’un des mécanismes les plus importants qui augmentent simultanément la résistance mécanique et la ductilité tout en conservant une excellente soudabilité de l’acier à faible teneur en carbone. On étudie l’influence du TMP dans la région (α + γ) sur la microstructure et les propriétés mécaniques de l’acier à faible teneur en carbone (LC). On a effectué le TMP par laminage à 760, 810 et 860 °C, avec différentes quantités de réduction, suivi par la trempe à l’eau. On a maintenu la vitesse de laminage à 5 m/min. Les résultats ont montré qu’on obtenait une résistance mécanique élevée avec une bonne élongation en utilisant la déformation intercritique à 810 °C et 70% de réduction totale par laminage. |
| |
Keywords: | |
|
|