Silver cementation from thiocyanate solutions by magnesium

Abstract

The cementation of silver on rotating magnesium disc from 0·005–0·02M thiocyanate solution was studied. It was established that the process proceeded with a high rate in the absence of the induction period. Metal recovery was >99%. The formation of dispersed porous deposits and the dependence of their structures on the initial concentration of silver ions were shown using SEM. The cementation product is silver powders with purity ≥99·9 mass-%. Consumption of magnesium is 0·15–0·2 g magnesium in account of 1 g of obtained silver.

On a étudié la cémentation de l’argent sur disque rotatif en magnésium à partir d’une solution de thiocyanate de 0·005–0·02M. On a établi que le procédé se produisait à grande vitesse sans période d’induction. La récupération du métal était >99%. On a démontré la formation de dépôts poreux dispersés et la dépendance de leurs structures sur la concentration initiale d’ions d’argent en utilisant le SEM. Les produits de cémentation sont des poudres d’argent ayant une pureté de ≥99·9% (en masse). La consommation de magnésium était de 0·15 à 0·2 g par g d’argent obtenu.