MICROSTRUCTURE AND MECHANICAL BEHAVIOUR OF Ni-ALLOYED AUSFORMED AUSTEMPERED DUCTILE IRON

Abstract

The abrasion wear behaviour of ausformed austempered ductile iron (AADI) as well as conventional austempered ductile iron (ADI) was investigated. The effects of both Ni content and rolling reduction during the ausforming process on wear resistance of AADI and ADI were studied thoroughly. The ausforming process has created a finer and more homogeneous ausferrite structure that has a direct influence on the mechanical properties of AADI. Maximum hardness and tensile strength were obtained with a 35% rolling reduction. On the other hand, ductility and impact strength were reduced with increasing rolling reduction during the ausforming process. AADI showed superior abrasion wear resistance due to its finer and harder structure.

On a investigué le comportement de résistance à l’abrasion de la fonte ductile austénitoformée, à trempe étagée bainitique (AADI) ainsi que de la fonte ductile conventionnelle à trempe étagée bainitique (ADI). On a étudié à fond l’effet de la teneur en Ni ainsi que de la réduction par laminage lors du traitement d’austénitoformage sur la résistance à l’usure de l’AADI et de l’ADI. Le traitement d’austénitoformage créait une structure ausferritique plus fine et plus homogène qui a une influence directe sur les propriétés mécaniques de l’AADI. On a obtenu une dureté et une résistance à la traction maximales avec une réduction par laminage de 35%. D’un autre côté, la ductilité et la résistance à l’impact étaient réduites avec une augmentation de la réduction par laminage lors du traitement d’austénitoformage. L’AADI a montré une résistance supérieure à l’abrasion, grâce à sa structure plus fine et plus dure.