Effect of impurity additions on the remanence and coercivity of reduced hematite ores

Abstract

Synthetic ores of pure ferric oxide, and ferric oxide with additions of CaO, SiO₂, MnO₂ and TiO₂ were made up by sintering the mixtures at 1100°C. Subsequent crushing, grinding and screening yielded ores with particle between 149 and 208 microns. The ores were reduced to mainetite between 500°C and 1000°C in a CO-CO₂ atmosphere.

The coercive force and remanence of the reduced ores were determined using a 60 cps hysteresis loop tracer. The addition of CaO decreased the coercive force and remanence of the reduced ore as compared to pure magnetite, whereas the effects of the other additions were not significant. Explanations for the findings are offered.

Résumé

Des minerais synthétiques d'oxide ferrique pur et d'oxyde ferrique additionné de CaO, SiO₂, MnO₂ et TiO₂ ont été élaboré par frittage à 1100°C. Après broyage et tamisage, la tail1e des particules de minerai s' échelonnait de 149 à 208 microns. Ces minerais étaient ensuit réduits en magnétite à des températures variant de 500 à 1000°C en atmosphére de CO-CO₂.

La force coercitive et la rémanence des minerais ainsi réduits, on été mesurees it 60 htz sur une boucle d'hystérésis. On a trouvé qu'une addition de CaO fait diminuer la force coercitive et la rémanence des minerais réduits par rapport à la magnétite pure, tan dis que les effets des autres additions sont sans signification. Une interprétation des résultats est donnee.