Weld nugget formation and mechanical properties of three-sheet resistance spot welded low carbon steel

Abstract

In this paper, weld nugget formation and mechanical properties of 1·25/1·25/1·25 mm three-sheet low carbon steel resistance spot welds are investigated. Heat conduction from sheet/sheet interfaces (i.e. places with higher electrical resistance) to the geometrical centre of the joint and heat dissipation via water cooled electrodes play an important role in weld nugget growth of three-sheet resistance spot welding. It was shown that the fusion zone size along the sheet/sheet interface was greater than that of along geometrical centre of the joint leading to high tendency to interfacial failure. Fusion zone size at the sheet/sheet interface proved to be the most important controlling factor of mechanical performance of three-sheet spot weld in terms of peak load and energy absorption.

Dans cet article, on examine la formation du noyau de soudure et les propriétés mécaniques de trois tôles d’acier de 1·25–1·25–1·25 mm à faible teneur en carbone, soudées par points par résistance. La conduction de chaleur des interfaces tôle - tôle (c’est-à-dire les endroits ayant une résistance électrique plus élevée) vers le centre géométrique du joint et la dissipation de chaleur par l’intermédiaire d’électrodes refroidies à l’eau jouent un rôle important dans la croissance du noyau de soudure du soudage à trois tôles par points par résistance. On a montré que la taille de la zone de fusion au long de l’interface tôle - tôle était plus grande que la taille de la zone de fusion au long du centre géométrique du joint, donnant naissance à une tendance élevée à la défaillance interfaciale. Il s’est avéré que la taille de la zone de fusion à l’interface tôle - tôle était le facteur de contrôle le plus important du rendement mécanique de la soudure par points à trois tôles en ce qui a trait à la charge de pointe et à l’absorption d’énergie.