The kinetics of the reactions between silica and alumino-silicate refractories and carbon-saturated iron |
| |
Abstract: | AbstractThe rates of attack of silica and alumino-silicate refractories in iron-carbon melts were measured. An immersion technique with cylindrical specimens was used under both static and dynamic conditions. The rates of reaction were measured both by specimen weight-loss and by chemical analysis of the melt. Experiments were carried out at 1400, 1500 and 1600°C under an inert atmosphere. The rates were found to be independent of rotation speed up to 400 rpm and for concentrations of carbon (>2.3%) and silicon (<1.0%) in the melt. The results are interpreted in terms of chemical reaction control at the refractory/metal interface and the dissociation of silica is proposed as the controlling step. Résumé On a mesuré les vitesses d'attaque des réfractaires de silice et alumino-silicates dans des bains fer-carbone par une technique d'immersion, avec des échantillons cylindriques, dans des conditions statiques et dynamiques. Les vitesses de réaction ont été mesurées à partir de la perte de poids des échantillons et par analyse chimique du bain. Les expériences ont été faites à 1400, 1500 et 1600°C sous atmosphère inerte. Les vitesses se sont averées etre indépendantes de la vitesse de rotation jusqu'à 400 rpm pour des concentrations de carbone (72.3%) et silicium (< 1.0%) dans le bain. Les résultats ont été interprétes en termes de contrôle de la réaction chimique à l'interface réfractaire-métal et on propose que la dissociation de la silice est le facteur contrôlant. |
| |
Keywords: | |
|
|