Rate of Transfer of Manganese Across Metal-Slag Interface and Interfacial Phenomena

Abstract

The rate of oxidation of manganese in liquid iron by oxidizing slag and rate of reduction of manganese oxide in liquid slag by liquid iron were measured at 1873 K. At the same time the liquid iron-slag interface was observed by an X-ray TV and the shape of iron drops was photographed on a film to determine the interfacial tension. From the results of the rate measurements it was found that the reaction proceeded rapidly over the initial period in the case of oxidation, but not in the case of reduction. The rate of reaction was analysed on the assumption that the reaction was controlled by simultaneous transport of manganese and oxygen. The change of interfacial tension during a run was small in spite of the transfer of surface active oxygen.

Résumé

Les vitesses d'oxydation et de réduction du manganèse ont été mesurées à l'interface métal-scorie d'un bain de fonte liquide à 1873 K. Simultanément, l'interface fonte-scorie a été observée à l'aide d'une caméra de télévision R-X et les goutelettes de fonte photographiées afin de déterminer la tension interfaciale. A partir des résultats des vitesse de réaction, il s'est avéré que la réaction s'effectue rapidement lors de la période initiale d'oxydation, mais non lors de la réduction. La vitesse de la réaction a été analysée en supposant qu'elle était contrôlée par le transport simultané du manganèse et de l'oxygène. Le changement de tension interfaciale lors d'un essai étai faible malgré le transfert d'oxygène actif en surface.