Reactivity of silicon steels hot-dip galvanizing

Abstract

Excessive reactivity of silicon-bearing steels in hot-dip galvanizing is well known. No adequate explanation exists as to why silicon should be so effective in destabilizing the layers of Fe-Zn intermetallies allowing free access of zinc to the reaction interface and causing linear kinetics to persist throughout the galvanizing reactions. Another important aspect of the silicon effect is the formation of grey coatings.

Special galvanizing experiments combined with electron microprobe and scanning electron microscope analyses and a critical reconsideration of existing knowledge allow us to present a consistent mechanistic picture of the silicon-induced reactivity and grey-coating phenomena.

Résumé

La réactivité excessive des aciers con tenant du silicium, lors de la galvanisation par immersion, est bien connue. Il n'existe aucune explication satisfaisante de la grande efficacité du silicium pour provoquer l'instabilité des couches d'intermétalliques Fe-Zn. Cette instabilité permet au zinc d'atteindre librement l'interface de réaction, ce qui fait que la cinétique demeure linéaire tout au cours des réactions de galvanisation. De plus, le silicium a une influence importante sur la formation de revêtements gris

Des expériences spéciales de galvanization combinées avec des analyses à la microsonde et au microscope électronique à balayage et un examen critique des connaissances actuelles, nous permettent de suggérer une image logique des phénomènes de la réactivité engendrée par le silicium et du revêtement gris.