Phase constitution of some intermetallics in continuous quaternary pillar phase diagrams |
| |
Authors: | Hideki Hosoda Shuichi Miyazaki Yoshinao Mishima |
| |
Affiliation: | (1) Department of Materials Science and Engineering, The Ohio State University, 286 Watts Hall, 2041 College Road, Columbus, OH 43210-1178, USA |
| |
Abstract: | In order to express multicomponent phase relationships, a new type of phase diagram, named a “pillar phase diagram,” is proposed. The pillar phase diagram is a sort of quaternary and Brewertype phase diagram. A pillar phase diagram at a temperature is easily constructed by (1) composing three sides of Brewer-type ternary-phase diagrams along the periodic table and (2) piling triangles of general ternary phase diagrams along the periodic table. Using the pillar phase diagrams, systematic understandings of phase constitution and stability along the periodic table can be performed for (1) binary intermetallics containing ternary and quaternary additional elements and (2) ternary intermetallics containing quaternary elements. Thus, the diagrams are convenient in terms of alloy design of multiphase intermetallic alloys. In this paper, the concept and the construction method of the pillar phase diagrams are described, and some examples are shown for systems related with L12 Ni3Al, B2 NiAl, L21 Ni2AlTi, B2 NiTi, B2 FeTi, L10 TiAl, and L12 Al3Ti alloys. |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
|