CCT Curves of low carbon Mn-Si steels and development of water cooled bainitic steels |
| |
Authors: | XU Feng-yun WANG Yong-wei BAI Bing-zhe FANG Hong-sheng |
| |
Affiliation: | Key Laboratory for Advanced Materials of Ministry of Education, Department of Materials Science and Engineering, Tsinghua University, Beijing 100084, China |
| |
Abstract: | CCT curves of Mn-Si steels with different manganese contents or carbon contents were determined. The results show that the transformation range of bainite can be separated from that of ferrite when the manganese content approaches a certain content, and the incubation period of ferrite increases more significantly than that of bainite transformation with the increase of carbon content in Mn-Si steels. Furthermore, water-cooled bainitic steels without adding expensive alloying element were developed. Granular bainite was obtained when a bar with diameter of 300 mm was cooled by water, and a mixed microstructure of granular bainite and martensite was obtained in water-cooled plate with thickness of 40 mm. The developed water-cooled bainitic steels containing no expensive alloying element showed a good combination of strength and toughness. The tensile strength, yield strength, and toughness (A_(KU) at -20 ℃) of bar with diameter of 300mm after water cooling were higher than 850 Mpa, 620 Mpa, and 65 J, respectively, and those of plate with thickness of 40mm after water cooling were higher than 1000 Mpa, 800 Mpa, and 50J, respectively. |
| |
Keywords: | Bainitic steels water-cooling granular bainite CCT curves Mn-Si steel |
本文献已被 CNKI 维普 万方数据 ScienceDirect 等数据库收录! |
| 点击此处可从《钢铁研究学报(英文版)》浏览原始摘要信息 |
|
点击此处可从《钢铁研究学报(英文版)》下载全文 |
|