Sulfidation behavior of Ni-Cr-Mo alloys at 700°C

The effect of molybdenum additions 5, 10, 15, and 20 wt. %, on the sulfidation behavior of Ni-20Cr, and the effect of chromium additions, 5, 10, 15, and 20 wt.%, on the sulfidation of Ni-20Mo were studied in pure sulfur vapor at 700°C. In general, the alloys followed a linear or near-linear rate law, the sulfidation rate of Ni-20Mo being slightly less than that of Ni-20Cr. The alloys having the lowest ternary addition, e.g., Ni-Cr-5Mo and Ni-20Mo-5Cr. exhibited the most rapid reaction rates. The highest alloying additions of 20 wt.% had no appreciable benefit on reaction rates. Scale structures were complex but generally consisted of several layers. The outer layer was always NiS_1.03, although both binaries formed Ni₃S₂ within the NiS_1.03. An inner layer of Cr₃S₄ existed in which there was considerable dissolved molybdenum. A thin, intermediate layer of Cr₂S₃ generally formed between the Cr₃S₄ and the outer nickel sulfide. An innermost layer of MoS₂ formed on all alloys containing more than 10 wt. % Mo, and a second phase of Mo₂S₃ formed within the MoS₂ on Ni-20Mo. Although the scales changed with alloy composition, no significant changes in reaction rate were observed. Notable differences in both scale structure and reaction kinetics between this study and previous studies were apparent. The differences and possible reaction mechanisms are discussed.