Improvements on the mechanical properties and thermal shock behaviours of MgO-spinel composite refractories by ZrO2 incorporation

Microstructural features and improvements on the mechanical properties and thermal shock behaviours of MgO-spinel composite refractories with ZrO₂ addition were examined. ZrO₂ incorporation into MgO-spinel led to improvements around ∼1.5-fold ratios on mechanical properties, R_st values and thermal shock results. The basic parameters improving mechanical properties and thermal shock resistance of MgO-spinel-ZrO₂ composite refractories were determined as follows: (i) propagation of microcracks for a short distance by interlinking each other, (ii) stopping or deviation of microcracks when reaching pores or ZrO₂ particles, (iii) concurrent occurrence of mostly intergranular and some transgranular cracks on fracture surfaces, and with the addition of ZrO₂ (iv) the increase in bulk density, and (v) a significant decrease in MgO grain size. The improvements observed in thermo-mechanical properties confirmed that MgO-spinel-ZrO₂ refractories showed a low strength loss and high thermal shock damage resistance at high temperatures, leading to longer service lives for using industrial applications.