Microwave dielectric properties of BaO-2(1 − x)ZnO-xNd2O3-4TiO2 (x = 0-1.0) ceramics

Microwave dielectric properties of (1 − x)BaZn₂Ti₄O₁₁-xBaNd₂Ti₄O₁₂ (x = 0-1.0) ceramics were investigated by the solid-state reaction with the purpose of finding a microwave ceramics with high dielectric constant (?_r), high quality factor (Q × f) and low temperature coefficient of resonant frequency (τ_f). A two phase system BaZn₂Ti₄O₁₁-BaNd₂Ti₄O₁₂ was formed and SEM photographs show equiaxed BaZn₂Ti₄O₁₁ grains and columnar BaNd₂Ti₄O₁₂ grains. The microwave dielectric properties were strongly determined by the chemical composition. As increasing x from 0 to 1.0, the phase composition varied from pure BaZn₂Ti₄O₁₁, to the two phase system BaZn₂Ti₄O₁₁-BaNd₂Ti₄O₁₂ and then to pure BaNd₂Ti₄O₁₂. Therefore, the ?_r raised from 29.1 to 82.0 and the Q × f values decreased from 54,630 GHz to 8110 GHz, and the τ_f values increased from −29 ppm/°C to 94 ppm/°C. 0.8BaZn₂Ti₄O₁₁-0.2BaNd₂Ti₄O₁₂ ceramics sintered at 1250 °C for 2.5 h had ?_r = 39.1, Q × f = 37,850 GHz and τ_f = −9 ppm/ °C.