Study of crystal structure,dielectric, magnetic and magnetoelecrtic properties of xCoFe2O4-(1-x)Na0.5Bi0.5TiO3 composites

Multiferroic composites of spinel ferrite and ferroelectric xCoFe₂O₄ – (1-x)Na_0.5Bi_0.5TiO₃ (with x = 0.10,0.30,0.50) were efficiently prepared by standard solid state reaction mechanism. X-ray diffractometer was used to analyze crystal structure of the prepared composites. The observed XRD patterns of the composites comprise peaks of both the phases i.e. ferrite and ferroelectric, with no sign of secondary peaks. Rietveld refinement of XRD data further confirms the coexistence of these two phases with cubic (Fd3m) and rhombohedral (R3c) symmetry corresponding to ferrite and ferroelectric phase respectively. The 3-dimensional overview of crystal structure of pure CoFe₂O₄ and Na_0.5Bi_0.5TiO₃ and of composite 0.50CoFe₂O₄?0.50Na_0.5Bi_0.5TiO₃ is generated by using refined parameters. The dielectric constant (ε´) and dielectric loss (tanδ) values were recorded as a function of frequency ranging from 100?Hz to 7?MHz and at different temperatures. Both ε´ and tanδ follow dispersion pattern at lower frequencies while show frequency independent behavior at higher frequencies. The magnetic evaluation carried by analyzing M-H hysteresis loop reveals the ferrimagnetic characteristics of these composites. The highest value of magnetic moment is 1.12μ_B observed for composite 0.50CoFe₂O₄ – 0.50Na_0.5Bi_0.5TiO_3. Magnetoelectric (ME) voltage coefficient (α) was also demonstrated to observe the interaction between ferrite and ferroelectric phases. The highest value of α (72.72μV/Oe cm) is obtained for low ferrite composition 0.10CoFe₂O₄ – 0.90Na_0.5Bi_0.5TiO₃, which suggests the dependence of magnetoelectric response on the resistivity of the composites.