Optimal synthesis and new understanding of P2-type Na2/3Mn1/2Fe1/4Co1/4O2 as an advanced cathode material in sodium-ion batteries with improved cycle stability |
| |
Authors: | Shiyong Chu Shenying Wei Yubo Chen Rui Cai Kaiming Liao Wei Zhou Zongping Shao |
| |
Affiliation: | 1. Jiangsu National Synergetic Innovation Center for Advanced Materials (SICAM), State Key Laboratory of Materials-Oriented Chemical Engineering, College of Chemical Engineering, Nanjing Tech University, Nanjing 210009, P. R. China;2. College of Energy, Nanjing Tech University, Nanjing 210009, P. R. China;3. Department of Chemical Engineering, Curtin University, Perth, Western Australia 6845, Australia |
| |
Abstract: | A sol-gel method with ethylene diamine tetraacetic acid and citric acid as co-chelates is employed for the synthesis of P2-type Na2/3Mn1/2Fe1/4Co1/4O2 as cathode material for sodium-ion batteries. Among the various calcination temperatures, the Na2/3Mn1/2Fe1/4Co1/4O2 with a pure P2-type phase calcined at 900 °C demonstrates the best cycle capacity, with a first discharge capacity of 157 mA h g?1 and a capacity retention of 91 mA h g?1 after 100 cycles. For comparison, the classic P2-type Na2/3Mn1/2Fe1/2O2 cathode prepared under the same conditions shows a comparable first discharge capacity of 150 mA h g?1 but poorer cycling stability, with a capacity retention of only 42 mA h g?1 after 100 cycles. Based on X-ray photoelectron spectroscopy, the introduction of cobalt together with sol-gel synthesis solves the severe capacity decay problem of P2-type Na2/3Mn1/2Fe1/2O2 by reducing the content of Mn and slowing down the loss of Mn on the surface of the Na2/3Mn1/2Fe1/4Co1/4O2, as well as by improving the activity of Fe3+ and the stability of Fe4+ in the electrode. This research is the first to demonstrate the origin of the excellent cycle stability of Na2/3Mn1/2Fe1/4Co1/4O2, which may provide a new strategy for the development of electrode materials for use in sodium-ion batteries. |
| |
Keywords: | Sodium-ion battery Cathode material Excellent cycle stability |
本文献已被 ScienceDirect 等数据库收录! |
|