The homogeneity range and the microwave dielectric properties of the BaZn2Ti4O11 ceramics

Ceramics with a composition close to BaZn₂Ti₄O₁₁ were synthesized according to various substitutional mechanisms in order to verify an existence of a homogeneity range in the vicinity of this composition. Structural and microstructural investigations showed that the crystal structure of BaZn₂Ti₄O₁₁ was formed in the homogeneity range corresponding to the formula BaZn_2 − xTi₄O_11 − x (0 < x < 0.1). Densely sintered BaZn_2 − xTi₄O_11 − x (0 < x < 0.1) ceramics exhibited a dielectric constant around 30, τ_f = −30 ppm/K and high Q × f values, which increased from 68,000 GHz at x = 0 to 83,000 GHz at x = 0.05. Structurally, the deficiency of Zn in BaZn_2 − xTi₄O_11 − x (0 < x < 0.1) resulted in a slight decrease in the unit-cell volume. The influence of secondary phases in the BaZn₂Ti₄O₁₁-based materials on the microwave dielectric properties was also investigated. A presence of small amounts of ZnO, BaTiO₃, hollandite-type solid solutions (Ba_xZn_xTi_8 − xO₁₆) and BaTi₄O₉ caused a decrease in Q × f values.