Sinterability and dielectric properties of Ba0.55Sr0.4Ca0.05TiO3-CaTiSiO5-Mg2TiO4 composite ceramics

The composite ceramics of Ba_0.55Sr_0.4Ca_0.05TiO₃-CaTiSiO₅-Mg₂TiO₄ (BSCT-CTS-MT) were prepared by the conventional solid-state route. The sintering performance, phase structures, morphologies, and dielectric properties of the composite ceramics were investigated. The BSCT-CTS-MT ceramics were sintered at 1100 °C and possessed dense microstructure. The dielectric constant was tailored from 1196 to 141 as the amount of Mg₂TiO₄ increased from 0 to 50 wt%. The dielectric constant and dielectric loss of 40 wt% Ba_0.55Sr_0.4Ca_0.05TiO₃-10 wt% CaTiSiO₅-50 wt% Mg₂TiO₄ was 141 and 0.0020, respectively, and the tunability was 8.64% under a DC electric field of 8.0 kV/cm. The Curie peaks were broadened and depressed after the addition of CaTiSiO₅. The optimistic dielectric properties made it a promising candidate for the application of tunable capacitors and phase shifters.