Some features of the formation of A1N during the reduction-nitriding of ultrafinely divided alumina |
| |
Authors: | T Ya Kosolapova D S Yakovleva G S Oleinik T S Bartnitskaya N P Tel'nikova I I Timofeeva |
| |
Affiliation: | (1) Institute of Materials Science, Academy of Sciences of the Ukrainian SSR, Ukraine |
| |
Abstract: | Conclusions A study was made of the process of carbothermic reduction-nitriding of ultrafinely divided alumina in the temperature range 1200–1450 C. It was established that the carbothermic reduction-nitriding of ultrafinely divided alumina is accompanied by the formation of intermediate oxycarbide and oxynitride phases. This is a result of the alumina reduction process having a stepwise character and of the formation of solid solutions in the AI-O-N system. It is shown that the resultant aluminum nitride is in the form of polycrystalline particles. The sizes of the particles and of the grains in them are 1–3 and 0.01–0.2 m, respectively. With rise in nitriding temperature, the particles decrease and the grains increase in size.Translated from Poroshkovaya Metallurgiya, No. 11(263), pp. 14–19, November, 1984. |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
|