Electrical properties and stability of Dy2O3-doped ZnO–Pr6O11-based varistors

The electrical properties and DC accelerated aging characteristics of ZnO–Pr₆O₁₁-based varistors were investigated with various Dy₂O₃ contents and sintering times. It was found that the Dy₂O₃ content and sintering time significantly affected electrical properties and their stability. The nonlinear exponent with increasing Dy₂O₃ content varied with ∨-shaped, reaching maximum of 58.6 at 1.0 mol% Dy₂O₃ for varistors sintered for 1 h and with ∧-shaped, reaching maximum of 46.3 at 0.5 mol% Dy₂O₃ for 2 h. The leakage current was in the range of 0.1–1.1 μA for varistors sintered for 1 h and 0.3–2.4 μA for 2 h. The increase of sintering time led to lowering of nonlinearity. The varistors with 0.5 mol% Dy₂O₃ sintered for 2 h exhibited the good stability, under DC stress of 0.95 V _{1 mA}/150 °C/24 h.