Poly(α,α,α′,α′-tetrafluoro-p-xylylene)

Poly(α,α,α′,α′-tetrafluoro-p-xylylene) was prepared by the pyrolysis of cyclo-di-(α,α,α′,α′-tetrafluoro-p-xylylene) and by the pyrolysis of α,α′-bis(alkylsulfonyl)-α,α,α′,α′-tetrafluoro-p-xylene. The pyrolysis of α,α′-dibromo-α,α,α′,α′-tetrafluoro-p-xylylene also gave the polymer, but the method is less satisfactory. Poly(α,α,α′,α′-tetrafluoro-p-xylylene) shows remarkable thermal and oxidative stability at elevated temperatures. Useful mechanical and electrical properties are retained after aging for 3000 hr at 250° in air. After initial change due to crystallization, tensile strength remains near 10,000 psi, elongation above 5%, and dielectric constants and dissipation factors at approximately 2.4 and .001, respectively.