Fundamental characteristics of DRAM capacitor application of PLZT ultrathin films prepared by MOCVD

Lanthanum-modified lead zirconate titanate (PLZT) thin films (50 nm to 200 nm) were deposited on Pt/SiO₂/Si substrate by metal-organic chemical vapor deposition (MOCVD). The electrical properties of the films were investigated as a function of the La content or the substrate temperature. Ferroelectric PZT(0/50/50) films were obtained at substrate temperatures as low as 500 °C; their electrical characteristics improved with increasing substrate temperature. La exhibited adequate solid solution in the PZT above 650 °C. PLZT(15/45/55) films with a thickness of 100 nm were found to have good properties for application to the capacitors of dynamic random access memory (DRAM), namely, an effective charge density of 80 fF/μm², a permittivity of 1000, an SiO₂ equivalent thickness of 0.4 nm, and a leakage current density of 5 × 10⁻⁸ A/cm. Addition of La to PZT was effective in reducing the leakage current with an increase in the registration rate. RuO₂ and/or IrO₂ bottom electrodes for ferroelectric PLZT films were also investigated. The RuO₂ films were found effective as diffusion barriers for PLZT and MgO. Significant interdiffusion at RuO₂/Si and RuO₂/SiO₂ interfaces occurred during the deposition of PLZT films. Annealing of the RuO₂ film considerably depressed interface reactions. © 1998 Scripta Technica. Electr Eng Jpn, 122(1): 25–36, 1998