| Abstract: | The epoxy resin/curing agent/montmorillonite nanocomposite was prepared by a casting and curing process. The intercalation and exfoliation behaviors of epoxy resin in the presence of organophilic montmorillonite were investigated by X‐ray diffraction (XRD) and dynamic mechanical thermal analysis (DMTA). For the diethylenetriamine curing agent, the intercalated nanocomposite was obtained; and the exfoliated nanocomposite would be formed for tung oil anhydride curing agent. The curing condition does not affect the resulting kind of composite, both intercalation or exfoliation. For intercalated nanocomposite, the glass transition temperature Tg, measured by DMTA and affected by the curing temperature of matrix epoxy resin is corresponded to that of epoxy resin without a gallery. The α′ peak of the loss tangent will disappear if adding montmorillonite into the composite. It was also found that the Tg of the exfoliated nanocomposite decreases with increasing montmorillonite loading. © 2002 John Wiley & Sons, Inc. J Appl Polym Sci 84: 842–849, 2002; DOI 10.1002/app.10354 |