粉煤灰提铝残渣低温碱溶过程工艺研究
引用本文:杜艳霞,郭昭华,王永旺,陈东. 粉煤灰提铝残渣低温碱溶过程工艺研究[J]. 无机盐工业, 2019, 51(8): 69-72. DOI: 10.11962/1006-4990.2018-0519
作者姓名:杜艳霞  郭昭华  王永旺  陈东
作者单位:神华准能资源综合开发有限公司,内蒙古鄂尔多斯 010300
基金项目:国家科技部“十二五”科技支撑计划项目“高铝粉煤灰高效循环利用技术研究”(2011BAA04B05)
摘    要:循环流化床粉煤灰“一步酸溶法”提取氧化铝工艺过程中产生的尾渣主要成分为无定形二氧化硅,且具有较高的活性,是制备白炭黑、分子筛、硅酸钠水玻璃的理想原料。对该提铝残渣在氢氧化钠溶液中的溶出过程做了研究,探讨了液固比、碱浓度、溶出时间、溶出温度工艺条件对二氧化硅和氧化铝溶出效果的影响。研究结果表明:在氢氧化钠碱液的浓度为4 mol/L、反应温度为70 ℃、液固比为6、反应时间为4 h的条件下,二氧化硅的溶出率最高,达到93%。提铝残渣碱溶后固体渣经XRD分析,其无定形二氧化硅基本已溶出,剩余物主要为锐钛矿与莫来石等。

关 键 词:粉煤灰提铝残渣  碱溶  二氧化硅  氧化铝  溶出率  
收稿时间:2019-02-10

Study on alkali leaching process of aluminum extraction residue from fly ash at low temperature
Du Yanxia,Guo Zhaohua,Wang Yongwang,Chen Dong. Study on alkali leaching process of aluminum extraction residue from fly ash at low temperature[J]. Inorganic Chemicals Industry, 2019, 51(8): 69-72. DOI: 10.11962/1006-4990.2018-0519
Authors:Du Yanxia  Guo Zhaohua  Wang Yongwang  Chen Dong
Affiliation:Shenhua Zhunneng Resources Comprehensive Development Company Limited,Erdos 010300,China
Abstract:Mainly composed by amorphous silica and having higher activity,the residue from circulating fluidized bed ash detached Al2O3 with one-step acid dissolution method is ideal raw materials for preparation of silica,molecular sieve and Na2SiO3.The dissolving process of residue of fly ash in sodium hydroxide solution was studied.The influence of liquid-solid ratio,alkali concentrations,dissolving time and dissolving temperature on dissolution rate of SiO2 and Al2O3 was also discussed.The results showed that the dissolving ratio of silica in residue of fly ash could be more than 93%,when the concentration of sodium hydroxide was 4 mol/L,the reactive temperature was 70 ℃,the liquid-solid ratio was 6,and the reactive time was 4 h.The solid residue from alkali leaching process of aluminum extraction residue was analysized by XRD.Results showed that almost all of amorphous silica in the residue dissolved into the lye,and the alkali residue was comprised of anatase,mullite and so on.
Keywords:aluminum extraction residue from fly ash  alkali dissolution  silicon dioxide  aluminum oxide  dissolving rate  